Aluminium
Boiling Point: 2467°c
Melting Point: 660°c
Density: 2.7g/cm³
Thermal Conductivity: (300 K) 237 W·m−1·K−1
Young’s Modulus: 70GPa
Shear Modulus: 26GPa
Poisson Ratio: 0.35
Hardness
Vickers: 167MPa
Brinell: 245MPa

Copper
Boiling Point: 2567°c
Melting Point: 1083°c
Density: 8.95 g/cm³
Thermal Conductivity: (300 K) 401 W·m−1·K−1
Young’s Modulus: 110–128 GPa
Shear Modulus: 48 GPa
Poisson Ratio: 0.34
Hardness
Vickers: 369 MPa
Brinell: 874 MPa

Chromium
Boiling Point: 2672°c
Melting Point: 1857°c
Density: 7.19g/cm³
Thermal Conductivity: (300 K) 93.9 W·m−1·K−1
Young’s Modulus: 279 GPa
Shear Modulus: 115 GPa
Poisson Ratio: 0.21
Hardness
Vickers: 1060 MPa
Brinell: 1120 MPa

Cobalt
Boiling Point: 2870°c
Melting Point: 1495°c
Density: 8.9g/cm³
Thermal Conductivity: (300 K) 100 W·m−1·K−1

Young’s Modulus: 209 GPa
Shear Modulus: 75 GPa
Poisson Ratio: 0.31
Hardness
Vickers: 1043 MPa
Brinell: 700 MPa

Gold
Boiling Point: 2807°c
Melting Point: 1064°c
Density: 19.32 g/cm³
Thermal Conductivity: (300 K) 318 W·m−1·K−1
Tensile Strength: 120 MPa
Young’s Modulus: 78 GPa
Shear Modulus: 27GPa
Poisson Ratio: 0.44
Hardness
Vickers: 216 MPa
Brinell: ???MPa

Iron
Boiling Point: 2750°c
Melting Point: 1535°c
Density: 7.87 g/cm³
Thermal Conductivity: (300 K) 80.4 W·m−1·K−1
Tensile Strength: 140-720 MPa
Young’s Modulus: 211 GPa
Shear Modulus: 82 GPa
Poisson Ratio: 0.29
Hardness
Vickers: 608 MPa
Brinell: 490 MPa

Lead
Boiling Point: 1740°c
Melting Point: 327°c
Density: 11.35g/cm³
Thermal Conductivity: (300 K) 35.3 W·m−1·K−1
Tensile Strength: 14 MPa
Young’s Modulus: 16 GPa
Shear Modulus: 5.6 GPa
Poisson Ratio: 0.44
Hardness
Vickers: ?? MPa
Brinell: 38.3 MPa

Mercury
Boiling Point: 357°c
Melting Point: -39°c
Density: 13.55 g/cm³
Thermal Conductivity: (300 K) 8.30 W·m−1·K−1
Young’s Modulus: N/A
Shear Modulus: N/A
Poisson Ratio: N/A
Hardness
Vickers: N/A
Brinell: N/A

Molybdenum
Boiling Point: 4612°c
Melting Point: 2617 °c
Density: 10.22g/cm³
Thermal Conductivity: (300 K) 138 W·m−1·K−1
Young’s Modulus: 329 GPa
Shear Modulus: 126 GPa
Poisson Ratio: 0.31
Hardness
Vickers: 1530 MPa
Brinell: 1500 MPa

Nickel
Boiling Point: 2732°c
Melting Point: 1453°c
Density: 8.9g/cm³
Thermal Conductivity: (300 K) 90.9 W·m−1·K−1
Young’s Modulus: 200 GPa
Shear Modulus: 76 GPa
Poisson Ratio: 0.31
Hardness
Vickers: 638 MPa
Brinell: 700 MPa

Platinum
Boiling Point: 3825 °C
Melting Point: 1768.3 °C
Density: 21.45 g·cm−3
Thermal Conductivity: (300 K) 71.6 W·m−1·K−1
Young’s Modulus: 168 GPa
Shear Modulus: 61 GPa
Poisson Ratio: 0.38
Hardness
Vickers: 549 MPa
Brinell: 392 MPa

Silver
Boiling Point: 2162 °C
Melting Point: 961.78 °C
Density: 10.49 g·cm−3
Thermal Conductivity: (300 K) 429 W·m−1·K−1
Young’s Modulus: 83 GPa
Shear Modulus: 30 GPa
Poisson Ratio: 0.37
Hardness
Vickers: 251 MPa
Brinell: 24.5 MPa

Tin
Boiling Point: 2602 °C
Melting Point: 231.93 °C
Density: (grey) 5.77 g·cm−3
(white) 7.37 g·cm−3
Thermal Conductivity: (300 K) 66.8 W·m−1·K−1
Young’s Modulus: 50 GPa
Shear Modulus: 18 GPa
Poisson Ratio: 0.36
Hardness
Vickers: ?? MPa
Brinell: 51 MPa

Titanium
Boiling Point: 3287°C
Melting Point: 1668°C
Density: 4.5g/Cm³
Thermal Conductivity: (300 K) 21.9 W·m−1·K−1
Young’s Modulus: 116 GPa
Shear Modulus: 44 GPa
Poisson Ratio: 0.32
Hardness
Vickers: 970 MPa
Brinell: 716 MPa

Tungsten
Boiling Point: 5555 °C
Melting Point: 3422 °C
Density: 19.25 g/cm3
Thermal Conductivity: (300 K) 173 W·m−1·K−1
Young’s Modulus: 411 GPa
Shear Modulus: 161 GPa
Poisson Ratio: 0.28
Hardness
Vickers: 3430 MPa
Brinell: 2570 MPa

Vanadium
Boiling Point: 3407 °C
Melting Point: 1910 °C
Density: 6.0 g/cm3
Thermal Conductivity: (300 K) 30.7 W·m−1·K−1
Young’s Modulus: 128 GPa
Shear Modulus: 47 GPa
Poisson Ratio: 0.37
Hardness
Vickers: 628 MPa
Brinell: 628 MPa

Zinc
Boiling Point: 907 °C
Melting Point: 419.53 °C
Density: 7.14 g/cm3
Thermal Conductivity: (300 K) 116 W·m−1·K−1
Young’s Modulus: 108 GPa
Shear Modulus: 43 GPa
Poisson Ratio: 0.25
Hardness
Vickers: ??
Brinell: 412 MPa